600mm big diameter 440B stainless steel round bar with cheap price

Stainless steels are high-alloy steels with good corrosion resistance because of large amounts of chromium present in them. About 10% of chromium is present in most stainless steels. Stainless steels are available in three different groups based on their crystalline structure. These groups include martensitic, austenitic and ferritic. The combination of martensitic and ferritic steels forms a fourth group of stainless steels known as precipitation-hardened steels. Grade 440B stainless steel is a high carbon martensitic stainless steel containing good strength, moderate corrosion resistance and ability to obtain and maintain wear resistance and excellent resistance.

Products Details

The mechanical properties of grade 440B stainless steel are displayed in the following table.
Properties Metric Imperial
Elastic modulus 190-210 GPa 27557-30458 ksi
Poisson's ratio 0.27-0.30 0.27-0.30
▪ Measuring instruments ▪ gage blocks ▪ Cutlery ▪ Knives ▪ Dies ▪ Molds ▪ Ball bearings and valve components.
440B stainless steel strip sizes and specifications
Grade 440B
Cold rolled stainless steel strip Thickness: 0.3mm- 3.0mm, Width: 5mm - 900mm,Surface: 2B/BA/SB/8K/HL/1D/2D etc
Hot rolled stainless steel strip Thickness: 3.0mm - 16mm, Width: 10mm - 900mm Surface: No.1/pickling
Stainless steel foil Thickness: 0.02mm- 0.2mm, Width: Less than 600mm, Surface: 2B
Standard ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303,  BS 1449, DN17441, G4305
440B stainless steel coil sizes and specifications
Grade 440B
Cold rolled stainless steel coil Thickness: 0.3mm- 3.0mm, Width: 1000mm - 2000mm,Surface: 2B/BA/SB/8K/HL/1D/2D etc
Hot rolled stainless steel coil Thickness: 3.0mm - 16mm, Width: 1000mm - 2000mm Surface: No.1/pickling
Standard ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303,   BS 1449, DN17441, G4305
440B stainless steel pipe sizes and specifications
Grade 440B
Stainless steel seamless pipe Outside diameter: 4.0 - 1219mm, Thickness: 0.5 -100mm,Length: 24000mm
Stainless steel welded pipe Outside diameter: 6.0 - 2800mm, Thickness: 0.3 -45mm,Length: 18000mm
Stainless steel capillary pipe Outside diameter: 0.4 - 16.0mm, Thickness: 0.1 -2.0mm,Length: 18000mm
Stainless steel welded sanitary pipe Outside diameter:8.0- 850mm, Thickness: 1.0 -6.0mm
Stainless steel seamless sanitary pipe Outside diameter: 6.0- 219mm, Thickness: 1.0 -6.0mm
Stainless steel square pipe Side Length: 4*4 - 300*300mm, Thickness: 0.25 - 8.0mm, Length: 18000mm
Stainless steel rectangular pipe Side Length: 4*6 - 200*400mm, Thickness: 0.25 - 8.0mm, Length: 18000mm
Stainless steel coil pipe Outside diameter: 0.4 - 16mm, Thickness: 0.1 - 2.11mm
Standard American Standard: ASTM A312, ASME SA269, ASTM A269, ASME SA213, ASTM A213 ASTM A511 ASTM A789, ASTM A790, ASTM A376, ASME SA335, B161, SB163, SB338, SB667/668 Germany Standard: DIN2462.1-1981, DIN17456-85, DIN17458-85· European Standard: EN10216-5, EN10216-2 Japanese Standard: JIS G3463-2006, JISG3459-2012 Russian Standard: GOST 9941-81
440B stainless steel profile sizes and specifications
Grade 440B
Specification EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO
Standard ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 .
Stainless steel round Bar Diameter: 2mm - 600mm
Stainless steel bright Bar Diameter: 2mm - 600mm
Stainless steel hex Bar Dimension: 6mm - 80mm
Stainless steel square bar Dimension: 3.0 - 180mm;
Stainless steel flat bar Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm
Stainless steel angle bar as requirements
Length Normally 6m, or produce as requirements
Surface Black, Bright. Peeled and Polished, Solution annealed.
Delivery condition cold drawn, hot rolled, forged, grinding, centerless grinding
Tolerance H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients’ requirements

The chemical composition of grade 440B stainless steel is outlined in the following table.

Element Content (%)
Iron, Fe 80
Chromium, Cr 16.0-18.0
Manganese, Mn 1.0
Silicon, Si 1.0
Carbon, C 0.75-0.95
Molybdenum, Mo 0.75
Phosphorous, P 0.040
Sulfur, S 0.030
Equivalent materials to grade 440B stainless steel are given in the table below.
AISI 440B ASTM A276 ASTM A314 ASTM A473
DIN 1.4112 QQ S763 FED QQ-S-763 MIL SPEC MIL-S-862
SAE J405 (51440B) SAE 51440B ASTM A580
Grade 440B stainless steel is annealed at 843-871°C (1550-1600°F) and then cooled very slowly in a furnace.Grade 440B stainless steel can be slightly cold worked by common cold working methods.Welding is not generally recommended for grade 440B stainless steel as it tends to harden in air. If this steel grade is welded the recommended temperature is 260°C (500°F) and for the post weld treatment the recommended temperature is 732-760°C (1350-1400°F). The post weld treatment should take place for 6 h and then the material should be cooled slowly in a furnace to avoid cracking. Similar high heat inputs and filler metal should be used during operations.Grade 440B stainless steel is best machined in the annealed condition. Chip breakers are used to handle tough, stringy chips of grade 440B stainless steel. Ceramic or carbide tooling is best suited for this grade 440B stainless steel.Hot working for grade 440B stainless steel takes place by pre-heating the steel to 760°C (1400°F) which is then followed by slowly increasing the temperature range to 1038-1204°C (1900-2200°F). After the hot working process, the material is then cooled slowly at room temperature followed by complete annealing.Grade 440B stainless steel is heated at 760°C (1400°F), soaked at 1010°C (1850°F) and finally cooled in oil or air.