Hastelloy X supplier,high quality hastelloy X ,nickel alloy X strip,HX alloy plate

The Hastelloy X nickel alloy, with higher iron content, has favorable resistance to oxidation and corrosion combined with excellent creep and rupture strength at temperatures under 900℃. In addition to this, Hastelloy alloy X has great fabricability by cold and hot working and good weldability. 1. High degree of oxidation resistance up to 2200° F 2. Outstanding high-temperature strength 3. Easily fabricated including forming and welding 4. Good ductility after prolonged exposure at high-temperatures 5. Good resistance to chloride stress-corrosion cracking 6. Resistant to carburization and nitriding 7. Develops a protective oxide film that does not spall off

Products Details

N06602 2.4665
Composition Ni Cr Fe Mo W Co C Mn Si S Cu Al Ti
Content (%) Min. Bal. 20.5 17.0 8.0 0.2 0.5 0.05            
  Max.   23.0 20.0 10.0 1.0 2.5 0.15 1.0 1.0 0.015 0.5 0.15 0.5
Tensile Strength (σb/MPa) Yield Strength (σp0.2/MPa) Elongation (σ5/%)
690 275 30
Bar Sheet/Strip Wire Pipe
This oxidation resistant alloy can be used for combustor components and other high temperature parts of aircraft engines, for long term use at temperature under 900℃ and short time use up to 1080℃. 1.Gas turbine engines 2.Transition ducts 3.Combustor cans 4.Spray bars and flame holders 5.Afterburners, tailpipes, and cabin heaters 6.Chemical processing retorts, muffles, and tubing
Hastelloy X available sizes and specifications
Grade Hastelloy X
Nickel plate Thickness: 0.3mm - 150.0mm Width: 1000mm - 3000mm
Nickel strip/ nickel foil Thickness: 0.02mm - 16.0mm Width: 5mm - 3000mm
Nickel coil Thickness: 0.3mm - 16.0mm Width: 1000mm - 3000mm
Nickel pipe Outside diameter: 6mm - 1219mm Thickness: 0.5mm - 100mm
Nickel Capillary Pipe Outside diameter: 0.5mm - 6.0mm Thickness: 0.05mm - 2.0mm
Nickel bar Diameter: Ф4mm - Ф600mm
Nickel wire rod Diameter:Ф0.01mm - Ф6mm